老翻砂匠 发表于 2023-2-26 10:28:18

球墨铸铁碳当量的选择【张伯明】

球墨铸铁碳当量的选择

https://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/5f697125-2a04-474d-b786-ed35c51d2074.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/d7ccb91a-bf93-409c-8131-7e9564698397.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/4cfa5bc6-0350-4db8-865c-2625aa70bfbd.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/01fb5064-eec3-4725-95e1-3baa8c2dbfb9.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/9012a2a0-b45b-4efb-bc0e-7bc22555956e.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/8dcc6680-7424-456d-9ebd-4e9fa3f48008.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/cb39ef5b-1b83-4377-b5e4-03bebdcdf15c.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/5831791a-d193-46b0-aef2-47654a58f39f.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/c32e9ded-033e-4319-95f6-9e99ea4f2d68.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/6eba1e4f-1271-469b-a3c8-59c697ed836a.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/485b56ba-96fd-4364-a0ef-ac215820fa48.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/31620364-60ed-4993-919d-eeba93335340.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/5bd9275c-c9d5-437e-a73c-9427e8dff6a1.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/4f5c94ef-cd33-47d9-8106-0653e8b77ab6.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/b1936560-f3c1-4ead-9718-6b9e46a3170e.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/46ed6599-81dd-4ae0-8111-e43d7c96ee52.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/b69f5b79-c819-4785-ad4a-7d1687ee34ec.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/e9339586-a28c-48b4-b2bd-6bac0c961761.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/f3f3ea71-0e4f-46f4-aaed-ab5501a693a5.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/51c6e559-b2f1-4afd-8a20-c38b5cb0cf59.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/d617247c-fd35-426e-8902-336057d0ba73.jpghttps://omo-oss-image.thefastimg.com/portal-saas/new2022022817514073722/cms/image/1de56696-ed51-4ad8-bf4b-9b1e444a8107.jpg

nthdnhb1979 发表于 2023-2-26 10:45:18

再次复习一下成分性能关系。感谢楼主

老翻砂匠 发表于 2023-2-26 11:18:46

nthdnhb1979 发表于 2023-2-26 10:45
再次复习一下成分性能关系。感谢楼主

不谢，张院长的这一组图（曲线）很经典，绝对受用！

xuwu531 发表于 2023-2-26 15:00:34

有原版PPT就好了，曲线不太清楚

老翻砂匠 发表于 2023-2-26 15:31:44

xuwu531 发表于 2023-2-26 15:00
有原版PPT就好了，曲线不太清楚

最经典的那张，可以在论坛的微信公众号（微信号：RJGRZM）搜索到的，应该出现过不少次，仅我就上传过不下于3次了。

DDFMA 发表于 2023-3-16 13:46:50

非常好

高山流水 发表于 2023-3-16 15:16:46

看红色提示部分

老翻砂匠 发表于 2023-3-16 16:45:57

高山流水 发表于 2023-3-16 15:16
看红色提示部分

应该是3.91，估计是字误。

alanli 发表于 2023-12-28 11:02:20

则转变为共晶石墨的碳的数量是
4.6－（2.4÷3）－－｛×20%｝
                        = 3.8－1.3－0.76 = 2.424 %。
按此公式计算结果为1.74，而不是2.424，怎么理解？@老翻砂匠

老翻砂匠 发表于 2023-12-28 13:02:13

alanli 发表于 2023-12-28 11:02
则转变为共晶石墨的碳的数量是
4.6－（2.4÷3）－－｛×20%｝
                        = 3.8 ...

感谢反馈~

应该是有错误的，不知道在什么时候转这个的截图就已经有问题了，我也尽量找找看。

xuwu531 发表于 2023-12-29 22:38:02

本帖最后由 xuwu531 于 2023-12-29 22:42 编辑

老翻砂匠 发表于 2023-12-28 13:02
感谢反馈~

应该是有错误的，不知道在什么时候转这个的截图就已经有问题了，我也尽量找找看。 ...

会不会是排版错误“4.6－（2.4÷3）－－｛×20%｝
                        = 3.8－1.3－0.76 = 2.424 %。”2%排成20%
如果是2%    原式=3.8-1.3-0.076=2.424

老翻砂匠 发表于 2023-12-30 11:25:40

xuwu531 发表于 2023-12-29 22:38
会不会是排版错误“4.6－（2.4÷3）－－｛×20%｝
                  ...

对的，问题就是错在这儿，2%的话，与后面的注解就能吻合上了，而20%确实太夸张了！

感谢您的提醒！:handshake