型砂管理手册一

zhd0221

1.0        L.O.I. OF RECYCLED SAND 再生砂的灼烧减量

2.0        PURPOSE 目的

2.1        To monitor the binder residue in reclaimed sand. Objective is to keep LOI as low as is
possible. High LOI affects the fluidity of the mixed sand (more difficult to flow and to fill in deep corners, pockets, etc) and the bulk density of the filled sand. High LOI also decreases the sand mechanical strength, and further causes Gas defects in castings.
        监察再生砂的树脂残留量。目标是把灼烧减量保持在最低水平。高灼烧减量影响树脂砂的流动性能
        （对较深处、冷角处充砂较困难）和降低型砂密度。高灼烧减量也使树脂砂的強度减弱，并增加气
        孔缺陷的机率。

3.0        TARGET RESULTS 目标成绩

3.1        Target to <2.5% 目标是少于百分之２.５
3.2         Beyond 3.0% will lead to weaker sand strengths, hence weaker molds/cores, tendency to metal penetration and gas defects
如果超过百分之３、砂強度将减弱、造成模与芯强度不足，增加粘砂和气孔缺陷的机率。
3.3        Nitrogen level in reclaimed sand <0.15%
              再生砂的含氮量应该少于百分之０．１５。

4.0        TEST PROCEDURES 检验手册

4.1        Laboratory procedures
实验室检验手册
4.2        At least once per week. More tests will be necessary when results are continuously beyond higher limits, or show an upward trend.
每周最少检测一次，如果检验结果一直保持在上限或是有上升趋势，必须增加检验频率。
4.3        Analyse sand sample before Reclaimer, and sand sample after Reclaimer. This is to monitor the efficiency of the Reclaimer. The Reclaimer must be calibrated to perform at manufacturer’s specifications.
砂再生前后样本检验可鉴定再生系统的效率，再生系统必须调试至功率符合作业标准。
4.4        Nitrogen analysis is outsourced from external Laboratory. Frequency: quarterly when condition is stable. Increase the frequency when LOI constantly high, or previous reading was high.
定期检验砂的含氮量。当含氮平稳时、频率应为每季度一次。如果灼烧减量持续偏高或前次检验结果顕示偏高，必须增加检验频率。

5.0        DATA COLLECTION 资料收集

5.1        Results to be plotted on Control Chart for monitoring.
      把结果以图表方式展示、便利于监察。

6.0        READINGS 数据
6.1        Target Result to be <2.5% 目标成绩必须少于百分之２.５。
6.2        An upward trend will indicate 如果数据上升示意。
a.        deteriorating efficiency of Reclaimer. 再生系统功能退化。
b.        excessive usage of Resin, hence resin residues had built up。
过量使用树脂、造成残留增加。
c.        excessive Sand-to-Metal Ratios. 砂铁配比太大。



7.0        FACTORS INFUENCING LOI 影响灼热减量的因素

7.1        Continual improvement to keep Sand-to-Metal Ratio low. Target 3:1
改善并降低砂铁配比率、目标为３：１。
7.2        Ensure New Sand addition is implemented accurately and correctly
确保新砂的加入量准确与正确执行。
7.3        Efficiency of Reclaimer
再生系统的效率。
7.4        Optimum Resin Dosage
      树脂的最佳使用量。

yang888

英汉对照，请楼主继续。

windak

想问下哪位有检测再生砂的经验？在检测覆膜砂的灼烧减量中我们的检测值在3%左右，但再生砂（焙烧后未覆膜）并未检测。

zhd0221

检验再生砂有一个国家标准，你可以在论坛里找一下，那个标准有详细的实验方法。

chine.cao

楼主能否说的详细一些呢?

ownyun

其实呢  如果有铝合金铸造件的话就采用金属型铸造，比壳型铸造先进多了！
现在金属型铸造工艺越来越成熟和普及，金属型模具制造成本越来越低，可是砂型铸造除了相当滴大批大量可以用流水线或者超大件外，其他的中低批量普通铸件还不如采用金属型重力浇铸的成本低质量好呢，不信的话就到周围同行那里看看！
    金属型铸造占用场地少、用人少、劳动强度低、招工容易、工本费用低、综合成本低、环保局找事少...............还是玩儿钢模好啊。。。

要是需要技术支持、熔炼保温炉、铸造机等设备的话可以找坛子里的高手帮忙上马，甚至可以协助建厂创业！！复杂的话就找个高手，不太复杂的就找个“中手”就是像我这样滴......联系......QQ  268039545

feixi

楼主中英文对照的资料是石墨资料？

qwsx

好，期待继续

qwsx

好，期待继续